Quality and Standards
Shivaline Multi layer Cross Laminated Tarpaulin (mXF) is manufactured by using judiciously chosen polymers suggested by experts, on skilfully designed machines with combination of technology and experienced team.
Our product are certified with IS Standard 14611:2016 (Multilayer Cross Laminated Film) vide Certificate number CML 7200 169611.
Technical Data Sheet of Multilayer Cross Laminated Film As per IS Standard
Characteristics | Requiements | ||
---|---|---|---|
Total Mass per Unit Area, Min, g/m2
|
LN (LIGHT DUTY) 60-100 GSM
|
MN (MEDIUM DUTY) 110-150 GSM
|
HN (Heavy Duty) 200-250 GSM
|
Centro comercial Moctezuma
|
Francisco Chang
|
Mexico
|
Mexico
|
Tensile Strength (kg/cm2, Min)
Longitudinal Direction
Transvers Direction
|
Kg/cm2
250
200
|
Kg/cm2
250
200
|
Kg/cm2
250
200
|
After ageing at 70 +/- 1°C FOR 168 h
Longitudinal Direction
Transvers Direction
|
30 % Decrease from the original
|
||
Elongation Break (%, Min)
Longitudinal Direction
Transvers Direction
|
%
400
300
|
%
400
300
|
%
400
300
|
Dart Impact Strength, g Min
|
250
|
400
|
%
400
300
|
Tear Strength, Min
Longitudinal Direction
Transvers Direction
|
g
1200
900
|
g
1280
1550
|
g
3000
1750
|
After ageing at 70 +/- 1°C FOR 168 h
Longitudinal Direction
Transvers Direction
|
30 % Decrease from the original
|
||
Dart Impact Strength, g Min
|
g 250
|
g 400
|
%
400
300
|
After ageing at 70 +/- 1°C FOR 168 h
Longitudinal Direction
Transvers Direction
|
40 % of the original strength
|
Shivaline V/s Conventional (Traditional) Tarpaulin
SHIVALINE | CONVENTIONAL TARPAULIN |
---|---|
Films multi orianted and cross laminated for
better strength
|
Made from woven sack polyethylene fabric
laminated with poly film
|
Cross Lamination in MD and TD so no possibility
of De- Lamination. Long product Life.
|
Due to Manufacturing process, product gets
delaminated, Very Fast product Ageing
|
Excellent weathering resistance due to Cross
Lamination in Md and TD both directions. No
Complaint of pin holes, cracks, shreds. Long
Lasting Product
|
Unidirectional Lamination develops pin holes
and crack and shreds. Poor weathering
resistance
|
Cross Lamination reduce thickness and reduce
weight.
|
Unidirectionally aligned layers makes it heavy
|
Excellent Sealing Property of product. Ultrasonic
welding provides full strength sealing of product.
|
Sealing property has poor life and stitching wear
off easily.
|
Excellent water and barrier property.
|
Poor water resistance and poor water barrier
property
|
Good weathering resistance even on direct
exposure to sunlight
|
Exposure to Sun / weather reduce product life
develops crack and shreds.
|
Ideally no eyelets attached so less possibility of
wear and tear of corner
|
Eyelet provided on reinforced sides may weak the
tarpaulin as it tears off easily.
|
Technological innovation provides precision on
Thickness/ GSM or New edge technology has
excellent control over strength, tolerance and
thickness (GSM).
|
GSM/Thickness variation issue.
|
SHIVALINE is light weight and easy to handle.
|
Other conventional tarpaulin like PVC Tarpaulin
are heavy, not moisture resistant and difficult to
handle.
|
Post service life, product is 100% recyclable,
environmentally sustainable and eco-friendly
|
Post Service waste generated is not eco-friendly.
|